Kapturek termokurczliwy z klejem
HSEC
- Material: Crosslinked polyolefin
- Cable end caps with spiral adhesive coating.
- Effectively offering protection against oxidation, ozone,
- UV Resistant
- Coated with conductive mastic to ensure environment seal
- Easily to fit into the cable end
- Min. full shrink temperature: 120ºC
| Part no. | Before hest shrink | After heat shrink | Cable dia. | |||
|---|---|---|---|---|---|---|
| D Min. dia. | D Max. dia. | A (±10%) | L (±10%) | Dw (±5%) | ||
| [mm] | ||||||
| HSEC-105-12-4 | 12 | 4.0 | 15 | 40 | 2.6 | 4-10 |
| HSEC-110-14-5 | 14 | 5.0 | 18 | 45 | 2.2 | 5-12 |
| HSEC-110L-14-5 | 14 | 5.0 | 30 | 55 | 2.2 | 5-12 |
| HSEC-115-20-6 | 20 | 6.0 | 25 | 55 | 2.8 | 6-16 |
| HSEC-120-25-8.5 | 25 | 8.5 | 30 | 68 | 2.8 | 10-20 |
| HSEC-130-35-16 | 35 | 16.0 | 35 | 83 | 3.3 | 17-30 |
| HSEC-130L-40-15 | 40 | 15.0 | 40 | 90 | 3.3 | 18-34 |
| HSEC-135-40-15 | 40 | 15.0 | 40 | 83 | 3.3 | 18-32 |
| HSEC-135L-42-15 | 42 | 15.0 | 40 | 110 | 3.3 | 18-34 |
| HSEC-140-55-26 | 55 | 26.0 | 50 | 103 | 3.5 | 28-48 |
| HSEC-140L-55-23 | 55 | 23.0 | 70 | 140 | 3.8 | 25-48 |
| HSEC-145L-62-23 | 62 | 23.0 | 70 | 140 | 3.8 | 25-55 |
| HSEC-150-75-36 | 75 | 36.0 | 55 | 120 | 4.0 | 45-68 |
| HSEC-150L-75-32 | 75 | 32.0 | 70 | 150 | 4.0 | 40-68 |
| HSEC-150XL-75-36 | 75 | 36.0 | 70 | 170 | 4.2 | 45-68 |
| HSEC-160-100-52 | 100 | 52.0 | 70 | 140 | 4.0 | 55-90 |
| HSEC-160L-105-45 | 105 | 45.0 | 65 | 150 | 4.0 | 50-90 |
| HSEC-170-120-60 | 120 | 60.0 | 70 | 150 | 4.0 | 65-110 |
| HSEC-180-145-60 | 145 | 60.0 | 70 | 150 | 4.0 | 70-130 |
| HSEC-190-160-82 | 160 | 82.0 | 70 | 150 | 4.0 | 90-150 |
Specyfikacja:
| Własności | Test | Wynik testu |
|---|---|---|
| Temperatura pracy | UL 224 | -55°C do ±110°C |
| Wytrzymałość | ASTM D 2671 | >13MPa |
| Wydłużenie | ASTM D 2671 | 300% |
| Starzenie cieplne | 158°C/168 hrs | >10MPa >250% |
| Wytrzymałość dielektryczna | IEC 243 | >15kV/mm |
| Oporność skrośna | ASTM D 2671 | >1013Ωcm |
| Absorbcja wody (23°C / 14 dni) | ISO 62 | <1% (max) |